Home Archive News Contact
PDF download
Cite article
Share options
Informations, rights and permissions
Issue image
Vol 13, Issue 1, 2021
Pages: 40 - 44
Research article
Metallic materials
See full issue

This is an open access article distributed under the Creative Commons Attribution License which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. 

Metrics and citations
Abstract views: 40
PDF Downloads: 24
Google scholar: See link
Article content
  1. Abstract
  2. Disclaimer
Published: 28.05.2021. Research article Metallic materials

HEAT RESISTANCE OF HK30Nb STAINLESS STEEL PIPE CASTING

By
Mirsada Oruč ,
Mirsada Oruč
Contact Mirsada Oruč

University of Zenica , Zenica , Bosnia and Herzegovina

Alen Delić ,
Alen Delić

TTUEnergetik,d.o.o. , Tuzla , Bosnia and Herzegovina

Almaida Gigovic-Gekic ,
Almaida Gigovic-Gekic

University of Zenica , Zenica , Bosnia and Herzegovina

Raza Sunulahpašić
Raza Sunulahpašić

University of Zenica , Zenica , Bosnia and Herzegovina

Abstract

The HK30Nb steel pipe casting was obtained by centrifugal casting. This steel is austenitic stainless steel grade AISI HK 30 and is standardized according to ASME SA-351 in as cast condition. HK 30 Nb steels not standardized i.e. it is HK 30 steel modified with niobium. In addition to the required mechanical properties, this steel is also tested for heat resistance because it is used at high temperatures. In this paper, the heat resistance testing was carried out on the HK 30 Nb stainless steel pipe casting for two temperatures (750 and 850 oC) according to the standard ASTM G 54-84. The mass change and rate of oxidation for different heating times (24, 48, 72, 96 and 120 hours) were determined. The results of the study are significant for the continued use of these materials at high temperatures in exploitation conditions. 

References

1.
Kostadin T. Čelici i željezni ljevovi-Materijali II, Veleučilište u Karlovcu. In: › fileadmin › user_upload › knjiznica › on_line_izdanjaMATERIJALI II KOSTADIN.pdf - Veleučilište u Karlovcu. 2017.
2.
M.Oruč Rs. M.Hadžalić: Ispitivanje materijala visokozahtjevnih komponenti, Fakultet za metalurgiju i materijale. 2016.
3.
A.Delić: Istraživanje odnosa između mikrostrukture i svojstava vatrootpornog austenitnog čelika HK 30 modificiranog niobijem u cilju poboljšanja svojstava na visokim temperaturama, Doktorska disertacija. 2018;
4.
Honeywell. IDM 8365: Cast Heat Resistant Nb Modified HK 30 Stainless Steel. 2012;
5.
G SASTM.
6.
G SASTM.
7.
A.Gigović-Gekić Mo. M.Gojić: Ispitivanje vatrootpornosti austenitnog nehrđajućeg čelika Nitronic 60. In: 11thInternational Foundrymen Conference. 2011.

The statements, opinions and data contained in the journal are solely those of the individual authors and contributors and not of the publisher and the editor(s). We stay neutral with regard to jurisdictional claims in published maps and institutional affiliations.