This paper is concerned with carburization heat treatment. Standard carburization generally entails several steps: carburization of the surface layer by carbon diffusion at high temperatures, subsequent hardening and stress relief. This combination of hard surface and resistance to breakage upon impact is useful in parts such as a cam or ring gear,...

By Belma Fakić, Mohamed Fadlalla Mohamed Ahmed, Babekir Ahmed Osman Mohammed, Faik Uzunović

In this paper the effect of different heat treatment (recrystallization, spheroidizing and normalizing) processes on microstructure of the steel DC04 intended for deep drawing is presented. The steel is cladded with CuZn10 layers by explosive welding. Since the melting temperature of alloy CuZn10 is significantly lower (melting range 1025-1045 oC) ...

By Omer Beganović, Belma Fakić, Ali Mohammed Ali Mohammedzain, Babekir Ahmed Osman Mohammed, Faik Uzunović

In this work, industrial control technical measurements of the heat treatment of high chromium steel (HCS) rolls is presented.Measurements were carried out on the gas fired car bottom chamber furnace Bosio PP-KP 70/1150 in the company Valji d.o.o., Štore, Slovenia. Temperature measurements of the individual heating zones of the furnace, roll...

By Blaž Karpe, Simon Rečnik, Aleš Nagode, Borut Kosec, Sergej Novak, Stjepan Kožuh

FeCrAl alloys have good oxidation resistance at elevated temperature owing to the formation of a continuous Al2O3 surface film, which acts as an oxygen diffusion barrier. The aim of the present study was to investigate the early stages of protective oxide layer formation and its growth on specially prepared commercial FeCrAl alloys, Kanthal AF (K-A...

By Stojana Veskovič, Milan Bizjak, Blaž Karpe, Aleš Nagode, Samo Smolej, Janez Kovač, Gorazd Kosec

Shape memory alloys (SMAs) belong to the group of advanced functional materials for numerous technical applications. Among many known Cu-based shape memory alloys, Cu–Al–Mn ternary alloys are characterized by a combination of good shape memory properties and excellent ductility which makes them commercially attractive.In this work the C...

By Dragan Manasijević, Tamara Holjevac-Grgurić, Ljubiša Balanović, Uroš Stamenković, Radiša Todorović, Milan Gorgievski1, Mirko Gojić

Successful examples of high–rise buildings in the world are obvious evidences that the use of high–strength concrete is nowadays reality in construction worldwide. Whether focus on high–rise buildings up to 15– 24 storeys, or the super tall high–rise buildings that are few hundred of storeys high, high–strength c...

By Ilda Kovačević, Sanin Džidić

Metallurgical coke, as a fuel and a reducing agent, also allows for the gas to go through a charge in the blast furnace. The coke must have a strength, porosity, reactivity and a uniform granulation, because reaction of CO2 at high temperatures in the furnace. There are various mathematical models for the optimization of coal blend, which allow the...

By Sulejman Muhamedagić, Mirsada Oruč, Admir Muminović, Amina Kurtović

Samples based on talc with 15 % of zeolite from Zlatokop, Serbia, sintered at 1200 ºC were prepared and tested in condition of cavitation erosion. The ultrasonic vibratory cavitation set up with stationary specimen was used. Mass loss was measured and degradation level of the samples using image analysis and Young modulus of elasticity was mon...

By Jelena Majstorović, Sanja Martinović, Milica Vlahović, Marina Dojčinović, Marko Pavlović, Tatjana Volkov Husović

The paper examined the conventional castables composed of a mixture of high aluminate cement with 70% Al2O3, chamotte waste with 42% Al2O3 and brick clay ,,Rapajlo“. The influence of particle size distribution on density, porosity, water absorption, modulus of rapture and cold crashing strength was investigated. Particle size distribution was...

By Marina Jovanović, Adnan Mujkanović, Nadira Bušatlić

The physical-mechanical properties of concrete with nanosilica were experimentally studied. Nanosilica in powder form was used as a partial replacement of cement at dosage of 3 and 6 wt.%. The experimental results show that the compressive strengths of concretes with nanosilica particles were all higher than those of reference concretes at ages 1, ...

By Adnan Mujkanović, Marina Jovanović, Amel Zahirović